Diferans ki genyen ant S235J0 akS235J0W se ke S235J0 se yon asye estriktirèl kabòn ak estanda a se EN 10025-2. S235J0W se dezagregasyon asye estriktirèl, estanda a se EN 10025-5.
Diferans nan konpozisyon chimik
EN 10025-2 S235J0 plak asye konpozisyon chimik
| Klas | Konpozisyon chimik | ||||||||
| S235J0 | Eleman Max (%) | ||||||||
| C | Si | Mn | P | S | N | Cu | |||
| Mwens pase oswa egal a 16 | ＞16 Mwens pase oswa egal a 40 | ＞40 | |||||||
| 0.19 | 0.19 | 0.19 | - | 1.50 | 0.040 | 0.040 | 0.014 | 0.60 | |
EN 10025-5 S235J0W konpozisyon chimik asye (%)
| Klas | Nimewo | C max. | Si max. | Mn | P | S max. | N max. | Kr | Cu |
| S235J0W | 1.8958 | 0.13 | 0.40 | 0.20 - 0.60 | max. 0.035 | 0.035 | 0.009 | 0.40 - 0.80 | 0.25-0.55 |
Diferans nan pwopriyete mekanik
EN 10025-2 S235J0 plak asye pwopriyete mekanik
| Klas | Pwopriyete mekanik | |||||||||||||
| S235J0 | Sede fòs mm Min Mpa |
Fòs rupture mm Min Mpa |
||||||||||||
| Mwens pase oswa egal a 16 | ＞16 Mwens pase oswa egal a 40 |
＞40 Mwens pase oswa egal a 63 |
＞63 Mwens pase oswa egal a 80 |
＞80 Mwens pase oswa egal a 100 |
＞100 Mwens pase oswa egal a 150 |
＞150 Mwens pase oswa egal a 200 |
＞200 Mwens pase oswa egal a 250 |
＞250 Mwens pase oswa egal a 400 |
＜3 | Pi gran pase oswa egal a 3 Mwens pase oswa egal a 100 |
＞100 Mwens pase oswa egal a 150 |
＞150 Mwens pase oswa egal a 250 |
＞250 Mwens pase oswa egal a 400 |
|
| 235 | 225 | 215 | 215 | 215 | 195 | 185 | 175 | - | 360-510 | 360-510 | 350-500 | 340-490 | - | |
EN 10025-5 S235J0W plak asye pwopriyete mekanik
| EN 10025-5 | Min. Sede fòs Reh MPa | Fòs Tensile Rm MPa | |||||||
| Epesè nominal (mm) | Epesè nominal (mm) | ||||||||
| Mwens pase oswa egal a 16 | >16 Mwens oswa egal a 40 | >40 Mwens pase oswa egal a 63 | >63 Pi piti oswa egal a 80 | >80 Mwens pase oswa egal a 100 | >100 Mwens pase oswa egal a 150 | <3 | >3 Mwens oswa egal a 100 | >100 Mwens pase oswa egal a 150 | |
| S235J0W | 235 | 225 | 215 | 215 | 215 | 195 | 360-510 | 360-510 | 350-500 |
Diferans nan aplikasyon an
S235J0 Ewopeyen estanda kabòn estriktirèl asye, 0 degre enpak, S235J0 yo itilize pou fabrike soude, boulon ak estrikti riveting. S235J0W se yon asye estriktirèl ki reziste -move tan ki amelyore sou baz S235J0.
S235J0Wse itilize pou soude, boulon ak riveting pati. Klas asye sa a amelyore kapasite pou reziste korozyon atmosfè nan tanperati anbyen.
Li se ajoute nan lòd yo reyalize rezistans korozyon. Sèten eleman alyaj espesifik, tankou P, Cu, Cr, Ni, Mo, elatriye, fòme yon kouch oksid pwoteksyon sou sifas metal la anba divès kondisyon klimatik.