1. Seleksyon Pwosesis soude
2. Filler Metal Seleksyon (Kritik pou Kowozyon Match)
Règ debaz: Sèvi ak filler ak Cu/P/Cr/Ni pou asire ke kouch rouye soude a matche ak metal debaz la epi evite korozyon galvanik.
SMAW: E7016‑G (AWS) / J507CrNiCu (GB); sèk nan 350-400 degre pou 1-2 èdtan, kenbe nan 100-150 degre nan yon fou tèmik.
GMAW/FCAW: ER50‑6NiCu (GMAW) oswa E81T1‑W2C (FCAW); sere nan resipyan ki fèmen pou anpeche absòpsyon imidite.
GTAW: ER50‑6NiCu (0.8-1.2 mm dyamèt) pou fèy mens ak pas rasin.
3. Preparasyon anvan soude
Netwayaj Sifas: Retire echèl moulen, rouye, lwil oliv, ak imidite nan 20 mm nan jwenti a lè l sèvi avèk yon bwòs fil, moulen, oswa sòlvan (asetòn/degreaser) pou anpeche porosite ak fann idwojèn.
Joint Design:
Butt joints: Square groove for t ≤6 mm (root gap 1–2 mm); V‑groove (60–70° included angle, 1–2 mm root face) for t >6 mm.
Jwenti file: Longè janm=0.7× epesè plak; jwenti lap min. sipèpoze 25 mm.
Tack soude: Sèvi ak menm filler ak soude prensipal la; longè 10-15 mm, espas 150-200 mm; retire tach ki defektye anvan soude prensipal la.
Prechofaj:
• Mwens pase oswa egal a 16 mm, tanperati ki pi gran pase oswa egal a 5 degre: Pa bezwen prechofe.
t >16 mm or ambient ≤0°C: Preheat to 80–150°C (use a pyrometer to verify); for t >25 mm, prechofe a 100-150 degre.
Chofe tout zòn jwenti a (Pi gwo pase oswa egal a 50 mm sou tou de bò) yon fason pou evite gradyan tèmik.
4. paramèt soude (chalè D' & Interpass kontwòl)
Antre Chalè: Keep at 15–25 kJ/cm (avoid >30 kJ/cm) pou anpeche grenn gra ak diminisyon nan HAZ la.
SMAW: 3.2 mm elektwòd → 100-140 A, 22-26 V, vitès vwayaj 150-200 mm / min.
GMAW: 1.0 mm fil → 180-220 A, 24-28 V, 20-25 L / min Ar + CO₂, vitès vwayaj 200-300 mm / min.
Tanperati Interpass: Kenbe nan 80-150 degre (maksimòm Mwens pase oswa egal a 200 degre) pou evite HAZ surchof; fre ak fòse lè si depase limit la.
Arc & Vwayaj: Sèvi ak kout arc pou diminye sal ak porosite; kenbe vitès vwayaj ki konsistan pou fòm pèl inifòm.
Multi-Pas soude: Netwaye salop byen ant pase; moulen nenpòt defo (egzanp, undercut, fizyon enkonplè) anvan pwochen pas la.
5. Tretman apre-soude
Tretman Imedya:
Remove slag, spatter, and weld spatter with a hammer, wire brush, or grinder; grind smooth any undercut >0.5 mm.
Gouge dèyè soude yon sèl bò pou retire defo rasin yo, apresa re-soude bò dèyè pou pénétration konplè.
Soulajman estrès:
For thick sections (t >20 mm) oswa estrikti ki gen anpil estrès: Tretman chalè apre soude (PWHT) nan 550-620 degre pou 1-2 èdtan pou chak 25 mm epesè, ki te swiv pa refwadisman founo a mwens pase oswa egal a 150 degre anvan refwadisman lè.
Pou seksyon mens (t Mwens pase oswa egal a 16 mm): Pa gen PWHT nesesè; sèvi ak pwosesis ki ba-idwojèn ak bon prechofe pou kontwole estrès rezidyèl.
Pwoteksyon korozyon:
PA penti soude a tout antye; olye de sa, aplike yon pasivatè asye dezagregasyon oswa akseleratè patina soude a ak HAZ ankouraje fòmasyon inifòm kouch rouye.
Nan zòn kotyè ki gen anpil sèl: Aplike yon glase mens ma transparan soude a pou amelyore rezistans korozyon san yo pa kache ayestetik rouye a.